Effect of the several epoxy resin-based sealer compositions on adhesion interface in radicular dentin after calcium hydroxide intracanal medication r…
2021
Made available in DSpace on 2022-04-29T08:32:43Z (GMT). No. of bitstreams: 0 Previous issue date: 2021-09-01 Background: This study evaluated the effects of several epoxy resin-based sealer compositions (AHP, AH Plus; ADS, Adseal; SPL, Sealer Plus) on bond strength and intratubular dentin penetration of the endodontic obturation, in root canal previously treated with calcium hydroxide intracanal medication (CH) and removed by continuous ultrasonic irrigation (CUI). Material and Methods: Forty-five maxillary canines were prepared up to F5 (ProTaper system), filled with CH, coronally sealed, and stored at 37ºC. After 1 week, CH was removed using 2.5% sodium hypochlorite energized by CUI. The …
In vitro antibacterial activity of endodontic sealers
2004
Summary Objectives To evaluate the antibacterial activity of four endodontic sealers: one epoxy resin sealer (AH Plus), two zinc oxide eugenol (ZOE)-based sealers (Endomethasone, Pulp Canal Sealer), and one sealer containing both ZOE and orthophenilphenol (Vcanalare). Methods A direct contact test (DCT) was performed. A 10 μl suspension of Enterococcus faecalis was placed on the test material 20 min, 24 h and 7 days after mixing. Bacteria were allowed to directly contact the sealers for 1 h at 37 °C. Bacterial growth was then spectrophotometrically measured every 30 min for 7 h, and again after 24 h as well. Results All freshly mixed sealers showed complete inhibition of bacterial growth. S…
Comparative Cytocompatibility and Mineralization Potential of Bio-C Sealer and TotalFill BC Sealer
2019
The aim of this study was to investigate the cytocompatibility and mineralization potential of two premixed hydraulic endodontic sealers compared with an epoxy resin-based root canal sealer. The cellular responses and mineralization capacity were studied in human periodontal ligament stem cells (hPDLSCs) that were exposed to premixed hydraulic sealers, Bio-C Sealer (Angelus, Londrí